Silver telluride

From Wikipedia, the free encyclopedia
(Redirected from Silver(I) telluride)
Silver telluride
Silver telluride
Names
Other names
Identifiers
3D model (JSmol)
ECHA InfoCard 100.031.277 Edit this at Wikidata
  • InChI=1S/2Ag.Te
    Key: YRXWPCFZBSHSAU-UHFFFAOYSA-N
  • [Ag][Te][Ag]
Properties
Ag2Te
Molar mass 341.3364 g/mol
Appearance grey-black crystals
Density 8.318 g/cm3
Melting point 955 °C (1,751 °F; 1,228 K)
3.4
Structure
Monoclinic, mP12
P21/c, No. 14
Except where otherwise noted, data are given for materials in their standard state (at 25 °C [77 °F], 100 kPa).
☒N verify (what is checkY☒N ?)

Silver telluride (Ag2Te) is a chemical compound, a telluride of silver, also known as disilver telluride or silver(I) telluride. It forms a monoclinic crystal. In a wider sense, silver telluride can be used to denote AgTe (silver(II) telluride, a metastable compound) or Ag5Te3.

Silver(I) telluride occurs naturally as the mineral hessite, whereas silver(II) telluride is known as empressite.

Silver telluride is a semiconductor which can be doped both n-type and p-type. Stoichiometric Ag2Te has n-type conductivity. On heating silver is lost from the material.

Non-stoichiometric silver telluride has shown extraordinary magnetoresistance.

Synthesis

[edit]

Porous silver telluride (AgTe) is synthesized by an electrochemical deposition method. The experiment can be performed using a potentiostat and a three-electrode cell with 200 mL of 0.5 M sulfuric acid electrolyte solution containing Ag nanoparticles at room temperature. Then a silver paste used in the tungsten ditelluride (WTe2) attachment leach into the electrolyte which causes small amounts of Ag to dissolve in the electrolyte. The electrolyte was stirred by a magnetic bar to remove hydrogen bubbles. A silver- silver chloride electrode and a platinum wire can be used as reference and counter electrodes. All the potentials can be measured against the reference electrode, and it was calibrated using the equation ERHE = EAg/AgCl + .059 pH + .197. In order to grow the porous AgTe, the WTe2 was treated using multiple cyclic voltammetry between -1.2 and 0 volts with a scan rate of 100 mV/s.[1]

Glutathione coated Ag2Te Nanoparticles can be synthesized by preparing a 9 mL solution containing 10 mM AgNO3, 5mM Na2TeO3, and 30 mM glutathione. Place that solution in an ice bath. N2H4 was added to the solution and the reaction is allowed to proceed for 5 min under constant stirring. Then the nanoparticles are washed three times by a way of centrifugation, after the three washes the nanoparticles are suspended in PBS and washed again with that same method.[2]

References

[edit]
  1. ^ Kwon, Hagyeong; Bae, Dongyeon; Won, Dongyeun; Kim, Heeju; Kim, Gunn; Cho, Jiung; Park, Hee Jung; Baik, Hionsuck; Jeong, Ah Reum; Lin, Chia-Hsien; Chiang, Ching-Yu; Ku, Ching-Shun; Yang, Heejun; Cho, Suyeon (2021-04-27). "Nanoporous Silver Telluride for Active Hydrogen Evolution". ACS Nano. 15 (4): 6540–6550. doi:10.1021/acsnano.0c09517. ISSN 1936-0851. PMID 33784072. S2CID 232429859.
  2. ^ Nieves, Lenitza M.; Dong, Yuxi C.; Rosario-Berríos, Derick N.; Mossburg, Katherine; Hsu, Jessica C.; Cramer, Gwendolyn M.; Busch, Theresa M.; Maidment, Andrew D. A.; Cormode, David P. (2022-08-03). "Renally Excretable Silver Telluride Nanoparticles as Contrast Agents for X-ray Imaging". ACS Applied Materials & Interfaces. 14 (30): 34354–34364. doi:10.1021/acsami.2c06190. ISSN 1944-8244. PMC 9482380. PMID 35867906.

See also

[edit]
[edit]